Type 316Ti is a titanium stabilized variation of alloy 316. This austenitic chromium-nickel stainless steel containing molybdenum which increases the corrosion resistance, improves resistance to pitting chloride ion solutions and provide increased strength at elevated temperatures. Properties are similar to those of alloy 316 except that 316Ti due to its Titanium addition can be used at elevated sensitization temperatures. Corrosion resistance is improved, particularly against sulfuric, hydrochloric, acetic, formic and tartaric acids, acid sulfates and alkaline chlorides.
UNS S31600/S31603,AISI 316/316L, SAE J405, SS316, 316SS, T 316, T 316L, T-316, T-316L, 18-12-3 Chromium-Nickel-Molybdenum,austenitic stainless steel
Products
We are suppliers of 316 stainless steel sheet, coil, and round bar, available in normal and 316L grades. Inventory sizes for both grades are available as shown below - please contact us for a quote on your material needs.
Purchase Stainless Angle Equal 316|Hex Bar 316|Rectangle Bar 316|Round Bar 316|Square Bar 316|Channel 316|Pipe 316|Perforated Sheet 316|Sheet/Plate 316|Threaded Rod 316|Coil Tube 316|Rectangle Tube 316|Round Tube 316|Square Tube 316|Ball 316|Bushing 316|Cap 316|Coupling 316|Cross 316|Elbow 316|Flange 316|Foil 316|Half Coupling 316|Nipple 316|Plug 316|Reducer 316|Tee 316|Union 316
In our extensive line of products, we offer stainless steel sheet and stainless steel plates.
Stainless steel sheet is typically sold in the annealed condition and is available in most grades. Our stainless steel sheets come in both a standard 2B finish and various polished finishes. Polished surfaces range from the standard #4 to a mirrored finish #8 and are usually covered with a removable vinyl coating. Our standard sheet sizes include 4' x 8', 4' x 10', and 5' x 10', but customized sizes are also available. Stainless steel plate is sold in the HRAP (Hot Rolled Annealed and Pickled) condition and finishes.
Like sheet, stainless steel plate comes in standard sizes varying in width from 4' to 8' and in length from 8' to 20', but can also be customized to suit the application. Stainless cut plate may be sheared in thicknesses up to 3/8", and plasma cut in thicknesses over that. Waterjet, band-saw, or laser cutting is also available. If you can't finThe most commonly used stainless steel alloy in the world, 304/304L stainless steel offers a great mix of strength and corrosion resistance without being overly specialized. It maintains excellent corrosion resistance in most situations outside of marine environments and maintains its properties in high temperature situations. It is typically used in aerospace, food and beverage industry, pressure containers, architectural designs and trim, cryogenic applications, and chemical processing equipment.d the size or grade that you're looking for, feel free to contact us for assistance.
Our stainless steel sheet selection includes a number of grades, cuts, sizes, and finishes that can be customized for the job at hand. The following is a list of some of our basic sheeting information:
Product | Stainless Steel Sheet/plate |
| grade | 200 series: 201/202 |
| 300 series: 301/304/304L/305/309S/310S | |
| /316/316L/316LN/316Ti/317/317L/347/347H | |
| 400 series: 405/409/409L/410/420/430/440C/444/4447 | |
| 600 series: 630/631 | |
| duplex stainless steel: 2205/2507/2520 | |
| super stainless steel: 904L | |
| technology | cold rolled/hot rolled |
| thickness | 0.1-150mm |
| width | 500-3000mm or as your requirement |
| surface treatment | 2B/hairline/8k mirror polished/NO.1/NO.4/BA |
| feature | high hardness and strength |
| /100% recycled | |
| /fire resistant/wter proof/anti corrosion | |
| /high temperature resistant | |
| /easy to clean and maintain | |
| /long lifetime/durable | |
| processing type | decoiling/cutting/welding |
| /surface grinding/bending | |
| MOQ | BA, 2B, 2D, 4K, 6K, 8K, NO.4, HL, SB, Embossed |
| Price term | CIF CFR FOB EXW |
| Payment term | under $10,000, pay in full by TT |
| over $15,000. 30%TT deposit in advance | |
| and 70%TT the balance before shipment | |
| Application | construction field, ships building industry, |
| petroleum,chemical industries, | |
| war and electricity industries, | |
| food processing and medical industry, | |
| boiler heat exchanger, machinery and hardware fields |
Here is a breakdown of the percentages of various elements used to create type316Ti steels:
| % | 316 | 316L | 316H | 316Ti |
| C | 0.0-0.07 | 0.0-0.03 | 0.04-0.08 | 0.0- 0.08 |
| Mn | 0.0-2.0 | 0-2.0 | 0.0-2.00 | 0.0-2.00 |
| Si | 0.0-1.0 | 0.0-1.00 | 0.0-1.00 | 0.0- 1.00 |
| P | 0.0-0.05 | 0.0-0.05 | 0-0.04 | 0.0-0.05 |
| S | 0.0-0.02 | 0.0-0.02 | 0.0-0.02 | 0.0-0.03 |
| Cr | 16.50-18.50 | 16.50-18.50 | 16.50-18.50 | 16.50- 18.50 |
| Mo | 2.00-2.50 | 2.00-2.50 | 2.00-2.50 | 2.00- 2.50 |
| Ni | 10.00-13.00 | 10.00-13.00 | 10.00-13.00 | 10.50- 14.00 |
| Ti | - | - | - | 0.40- 0.70 |
| Fe | balance | balance | balance | balance |
Density: 0.29 lbs/in³, 7.99 g/cm³
Electrical Resistivity: microhm-in (microhm-cm): 68°F (20°C): 29.4 (74.0)
Specific Heat: BTU/lb/°F (kJ/kg•K): 32-212°F (0-100°C): 0.12 (0.50)
Thermal Conductivity: BTU/hr/ft²/ft/°F (W/m•K): At 212°F (100°C): 9.4 (16.2) At 932°F (500°C): 12.4 (21.4)
Mean Coefficient of Thermal Expansion, in/in/°F (μm/m•K):
32-212°F (0-100°C): 8.9 x 10 (16.0)
32-600°F (0-315°C): 9.0 x 10 (16.2)
32-1000°F (0-538°C): 9.7 x 10 (17.5)
32-1200°F (0-649°C): 10.3 x 10 (18.5)
32-1500ºF (0-871ºC): 11.1 x 10 (18.5)
Modulus of Elasticity: KSI (MPa) 28.0 x 10³(193 x 10³) in tension
11.2 x 10³(77 x 10³) in torsion
Magnetic Permeability: H = 200 Oersteds: Annealed: < 1.02 max.
Melting Range: °F (°C) 2500 - 2590 (1371 - 1421)
Table 2.Typical mechanical properties for 316 stainless steelalloys
Grade | 316 Bar and Section (up to 160 mm thick) | 316 Sheet (up to 8 mm thick) | 316 Plate (8 - 75 mm thick) | 316L Bar and Section (up to 160 mm) | 316L Sheet (up to 8 mm thick) | 316 L Plate (8 - 75 mm thick) | 316H Bar (up to 160 mm) | 316Ti Bar(up to 160 mm) |
Tensile Strength (MPa) | 500 - 700 | 530 - 680 | 520 - 670 | 500 - 700 | 530 - 680 | 520 - 670 | 490 - 690 | 500 - 700 |
Proof Stress (MPa) | 200 Min | 240 Min | 220 Min | 200 Min | 240 Min | 220 Min | 205 Min | 200 Min |
Elongation A50 mm | 40 Min % | 40 Min % | 45 Min % | 40 Min % | 40 Min % | 45 Min % | 35 % | 40 Min % |
Hardness Brinell | 215 Max HB | - | - | 215 Max HB | - | - | - | 215 Max HB |
Ultimate Tensile Strength: 75 KSI min (515 MPa min)
Yield Strength: (0.2% Offset) 30 KSI min (205 MPa min)
Elongation: 40% min
Hardness: Rb 95 max
Properties: Tempered
1/16H
Ultimate Tensile Strength: 85 KSI min (585 MPa min)
Yield Strength: (0.2% Offset) 45 KSI min (310 MPa min)
Elongation: 35% min
1/8H
Ultimate Tensile Strength: 100 KSI min (690 MPa min)
Yield Strength: (0.2% Offset) 55 KSI min (380 MPa min)
Elongation: 35% min
1/4H
Ultimate Tensile Strength: 125 KSI min (860 MPa min)
Yield Strength: (0.2% Offset) 75 KSI min (515 MPA min)
Elongation: 10% min
Alloy 316Ti can be cold rolled to achieve the temper properties required by specific
customers and/or manufacturing requirements. Contact Ulbrich Wire for details
| Surface finish | Characteristics & Application |
| NO.1 | Hot-rolled surface,annealed and pickled,can be used as cold-rolling material,industial tanks and chem i cal devices. |
| NO.2D | Cold-rolled, an nealed and pick led with out skinpassing the dull prod ucts can be used as auto mo bile parts, build ing materrials and pipings. |
| NO.2B | The surface brightness and flatness of NO.2B is better than NO.2D. Then through a special surfacetreament to improve its mechamical properties, N02B could nearly satisfy com pre hen sive uses. |
| NO.3 | Polished with abra sive belt of grit #100#120,have bet ter bright ness with dis con tin u ous coarse stria, used as in ner and ex ter nal or na ments for building, elec tri cal ap pli anc es and kitchen uten sils etc. |
| NO.4 | Polished with abrasive belt of grit #150#180, have better brightness with discontinuous coarse stria, but thinner than NO.3, are used as bathtud buildinginner and external ornaments electrical appliances, kitchen utensils and food processing equipment etc. |
| HL | Polished with abrasive belt of grit #150-320 on the No.4 finish and has continuous streaks, mainly used as building ornaments, elevators, door of building, frontal plate etc. |
| BA | Cold rolled, bright an nealed and skin passed, the prod uct has ex cel lent bright ness and good re flex iv i ty like mirror, used for lectrical appliances, mirror, kitch en apparatus, or na ment ma te ri als etc. |